ASTM A533 Grade D CL2
ASTM A533/A533M A533 Grade D CLASS 2,ASME SA533/SA533M SA533GRDCL2 steel plate are mainly used for building pressure veesels with alloy elements Mn,Mo and Ni.Comparing with boiler steel plate A533GrDcl1,boiler steel plate A533GrDcl2 owned a higher yield strength(Min.485Mpa) and tensile strength(620-795Mpa),so pressure vessel steel plates also be named as high strength steel plates which can be bear the higher strength surroundings.Ultrasonice examination shall be done after rolled steel plates SA533GRDCL2.
Technical Requirements & Additional Services:
High tension test
- Conform to ASTM A20/A20M
- Low temperature impacting test
- Simulated post-welded heat treatment (PWHT)
- Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
- Shot blasting and Painting, Cutting and welding as per end user’s demands
Mechnical property for A533GrDCl2 boiler steel:
| Yield strength (≥Mpa) | Tensile strength (Mpa) | Elongation in ≥,% | |
| 485 | 620-795 | 200mm | 50mm |
| … | 16 | ||
Chemical composition for A533 Grade D Cl2 boiler steel (Product Analysis Max%)
| Main chemical elements composition of A533GrDCl2 | ||||||
| C | Si | Mn | P | S | Mo | Ni |
| 0.25 | 0.13-0.45 | 1.07-1.62 | 0.035 | 0.035 | 0.41-0.64 | 0.17-0.43 |
Steel Grade A533 Grade D Class 2 composition information, ASTM A533 Grade D Class 2 ASTM A533/A533M element content, ASTM A533 Grade D Class 2 ASTM A533/A533M Heat treatment, ASTM A533 Grade D Class 2 ASTM A533/A533M chemistry
| Element | Min | Max | Similar |
|---|---|---|---|
| Mo | 0.4500 | 0.6000 | – |
| Ni | 0.2000 | 0.4000 | – |
| P | – | 0.0350 | – |
| S | – | 0.0350 | – |
| Mn | 1.1500 | 1.5000 | – |
| Si | 0.1500 | 0.4000 | – |
| C | – | 0.2500 | – |
| Si | 0.1300 | 0.4500 | – |
| S | – | 0.0250 | – |
| P | – | 0.0250 | – |
| Ni | 0.1700 | 0.4300 | – |
| Mo | 0.4100 | 0.6400 | – |
| Mn | 1.0700 | 1.5000 | – |
ASTM A533 Grade D Class 2 ASTM A533/A533M Mechanical
The resistance of ASTM A533 Grade D Class 2 ASTM A533/A533M to damage under load is called its mechanical properties. The mechanical properties of steel materials are the main basis for the design and material selection of parts. The mechanical properties of steel materials will be different with different loading properties (such as tension, compression, torsion, impact and cyclic loads). Common mechanical properties include strength, plasticity, hardness, impact toughness, multiple impact resistance and fatigue limit.
The mechanical properties of ASTM A533 Grade D Class 2 ASTM A533/A533M is in line with ASTM A533/A533M. The main properties as below:
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 969 (≥) | 535 (≥) | 34 | 14 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 332 |
ASTM A533 Grade D Class 2 ASTM A533/A533M Physical
The ASTM A533 Grade D Class 2 ASTM A533/A533M material physical properties shall comply with the values given in the following table.
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 34 | – | – | 0.11 | – | |||
| 457 | 523 | – | 44.3 | 111 | – | ||
| 397 | – | 43 | 43.2 | 112 | 243 |