10CrMo910 is a high-pressure boiler steel grade, containing chromium and molybdenum as its main alloying elements.
10CrMo910, with increased molybdenum and chromium, provides greater heat and corrosion resistance than 16Mo3 & 13CrMo45. Again the material is a pressure vessel grade steel for use in elevated temperature service. We supplies 10CrMo910 to fabricators serving the oil and gas industry. The steel has good weldability and is offered under the EN 10028 standard.
10crmo910 alloy pipe is used for heating surface pipes of low and medium pressure boilers (working pressure is generally not greater than 5.88Mpa and working temperature below 450 ° C), for high pressure boilers (working pressure is generally above 9.8Mpa and working temperature is 450 – 650° C Between) heating surface pipes, economizers, superheaters, reheaters, pipes for petrochemical industries, etc.
| Grade | C | Si | Mn | P | S | Cr | Mo | Ni | N | Cu |
| 10CrMo910 | 0.08/0.14 | 0.5 | 0.40/0.80 | 0.02 | 0.01 | 2.00/2.50 | 0.90/1.10 | – | 0.012 | 0.3 |
| Thickness | Yield Strength | Tensile Strength | Elongation (A) |
| mm | MPa | MPa | % |
| ≤16 | 310 | 480/630 | 18 |
| >16 ≤40 | 300 | 480/630 | 18 |
| >40 ≤60 | 290 | 480/630 | 18 |
| >60 ≤100 | 280 | 470/620 | 17 |
| >100 ≤150 | 265 | 460/610 | 17 |
| >150 ≤250 | 250 | 450/600 | 17 |
| Thickness | -20°C | 0°C | +20°C |
| mm | J | J | J |
| ≤16 | – | – | 31 |
| >16 ≤40 | 31 | ||
| >40 ≤60 | 31 | ||
| >60 ≤100 | 27 | ||
| >100 ≤150 | 27 | ||
| >150 ≤250 | 27 |
10CrMo910 is commonly used for manufacturing of heating and ventilation systems, pressure vessels, and boilers that operate at high temperatures and high pressures. This grade can withstand high-temperature conditions up to 580°C and has good corrosion resistance and toughness.
Ceramic lined pipe is made through self-propagating high-temperature synthesis (SHS) technique.
Cast basalt lined steel pipe is composed by lined with cast basalt pipe, outside steel pipe and cement mortar filling between the two layers.
Ceramic tile lined pipes have very uniform coating of specially formulated ceramic material that is affixed to the inner of the pipe.
The material of the rare earth alloy wear-resistant pipe is ZG40CrMnMoNiSiRe, which is also the grade of rare earth alloy steel.
Tubes Erosion Shields are used to protect boiler tubing from the highly erosive effects of high temperatures and pressures thereby greatly extending tube life.
The ASTM A213 T91 seamless tubes are primarily used for boiler, superheater, and heat-exchanger.